Brass Plating Services and Brass Plating Solutions from Shiv Polishing Works

Brass Plating Services

With our immense domain expertise, we are engaged in offering quality brass plating services, brass plating solutions in which all parts are coated with specially prepared water-based acrylic lacquer that prevents them from tarnishing. Our services are rendered at a low temperature process operating at 105° F and can be used in both rack and barrel operations to attain highest level of client satisfaction.

	Brass Plating Services

Our Brass Plating Services are offered using technically advanced range of machines to produce a glossy as well as polished brass color. We make use of optimum quality brass and ensure no poor color, oxidized finishes and non uniformity is offered. After plating, parts are coated with specially prepared water-based acrylic lacquer that prevents them from tarnishing.

Types of plating:

E-Brite B-150 —Conventional cyanide plating process

E-Brite B-150 — is a conventional cyanide plating process
It plates twice as fast as any other cyanide brass process
It is a single additive process with excellent throwing power that produces a lustrous, highly desirable yellow-green, 70/30 brass color
It is a low temperature process operating at 105° F and can be used in both rack and barrel operations
The copper and zinc plate together in a uniform alloy composition over a wider current density and temperature range, thereby helping to reduce rejects due to poor color, non-uniformity and poorly oxidized finishes
The E-Brite B-150 utilizes electrosolv as an anode corroder which retards the growth of carbonates, plus in barrel brass lines utilizing electrosolv will eliminate the need for addition of copper and zinc cyanide when using 70/30 brass anodes

E-Brite BPA (Brass Passivating Agent)

An alkaline, chromate-based passivating solution for brass, bronze, copper and silver
It is used cathodically after plating to prevent spotting and bleed-out and preserves the original color of plated surfaces
It provides excellent short term protection for parts in processing with resistance to 100 hour salt spray and 500 hours of 100% humidity without a lacquer topcoat
It is the preferred agent for increased corrosion resistance for plated objects top-coated with a clear acrylic or epoxy lacquer and also for clear powder coatings
The use of BPA will double and even quadruple the life of a clear top-coat
It also works equally as well on solid wrought brass alloys and copper